Product Overview
Magnesia alumina spinel brick is an advanced refractory material. Generally, Mg-Al spinel refractory refers to the general structure of MgAl2O4 or MgO-Al2O3, that is, the magnesium aluminum spinel is prepared from high-purity materials, has good corrosion resistance, thermal shock stability. The amount of spinel content in the production of magnesia aluminum spinel brick should keep a proper level. As spinel amount increases, the thermal shock resistance is better, but the strength (especially the flexural strength) is caused by the mismatch expansion. The Al2O3 in the product should not be more than 15%~20%, preferably 10%~18%.
Product Characteristics
01.
Good corrosion resistance
02.
Strong thermal shock resistant ability
03.
Higher compressive strength
04.
Good wear resistance
05.
Chromium-free and environmental protection
Application
Magnesia alumina spinel brick is widely used in non-ferrous metal smelting furnace, steel-nickel furnace, aluminum-smelting furnace lining, electric furnace cover, steel drum lining, high-temperature zone in cement kiln, glass furnace kiln wall, etc.
Specification should be different according to different furnaces/kilns, standard shapes and customized drawings are acceptable.
Product Specifications
| Item | MGA-A | MGA-B | MGA-C |
| MgO% | 80-85 | 90 | 93 |
| Al2O3% | 9 | 5 | 5 |
| Bulk Density(g/cm3) | 18 | 18 | 18 |
| Refractoriness℃ | ≥1790 | ≥1770 | ≥1750 |
| Apparent porosity% | 2.85-2.9 | 2.9 | 2.95 |
| Cold Crushing Strength Mpa | 40 | 45 | 40 |
| Refractoriness Under Load (0.2Mpa) ℃ | 1650-1700 | 1700 | 1700 |